  • Preparation and properties of Al-Al2O3 metal ceramics via powder metallurgy methods
  • Jieguang Songa,*, Xiuqin Wangb, Lin Chena, Cailiang Panga, Jia Zhanga, Weiguo Shia, Songlin Guoa, Xianzhong Wanga and Ruihua Wangc
  • aEngineering & Technology Research Center for Environmental Protection Materials and Equipment of Jiangxi Province, School of Materials and Chemistry Engineering, Pingxiang University, Pingxiang 337055 China bLibrary of Pingxiang University, Pingxiang 337055 China cSchool of Mechanical and Materials Engineering, Jiujiang University, Jiujiang 332005 China
Abstract
Metal ceramics are outstanding new engineering materials that offer the advantages of both ceramics and metals. In this study, Al-Al2O3 metal ceramics were prepared through powder metallurgy methods, and the densification and properties of the prepared metal ceramics were investigated to gain insights into the preparation of high-performance cermet materials. Results revealed that as the forming pressure was increased, the relative density of the ceramics increased, whereas their electrical resistivity decreased. The relative density increased with increasing sintering temperature up to 700 oC and decreased beyond 700 oC, whereas the electrical resistivity exhibited an opposite trend. The relative density increased with increasing Al content, whereas the electrical resistivity displayed an opposite trend. Under optimal technological parameters of 700 oC sintering temperature, < 20MPa forming pressure, and 75 wt% Al content, Al-Al2O3 metal ceramics with a high relative density (97.52%) and a low electrical resistivity (101.34 Ω·m) were successfully prepared.

Keywords: Metal ceramics, Powder metallurgy methods, Alumina, Aluminum.

This Article

  • 2018; 19(1): 50-53

    Published on Feb 28, 2018