Articles - Electrochemical properties of Li2Mn1-xVxO3 (0 ≤ x ≤ 0.018) as cathode materials for secondary lithium batteries
- Kyung Wan Kang, Won-Tae Kim and Yeon Uk Jeong*
- School of Materials Science and Engineering, Kyungpook National University, Daegu 702-701, Korea
Abstract
Li2Mn1-xVxO3 (0 ≤ x ≤ 0.018) samples were synthesized at low temperature by solid-state reaction using precipitated products of Mn and V. Li2Mn1-xVxO3 samples had a single phase of monoclinic layered structure with a space group of C2/m, and the solubility limit of V was 1.8%. Compared to Li2MnO3 sample, V-doped samples exhibited improved electrochemical properties. The initial charge and discharge capacities of Li1.682Mn0.982V0.018O3 sample were 353 and 248 mAh/g, respectively
Keywords: Lithium-ion batteries, Cathode material, Li2MnO3, Crystal structure, Electrochemical properties.
This Article
Copyright 2019 International Orgranization for Ceramic Processing. All rights reserved.Clean-Energy Research Institute(CRI), Hanyang University, 222, Wangsimni-ro, Seongdong-gu, Seoul, 04763, Korea
E-mail: jcpr@hanyang.ac.kr